MAS Medium Hardener is a polyamine blend intended for moderate reactivity. Moderate pot life, gel, and thin film set times provide advantages when filleting and fairing. MAS Epoxy/Medium mixed with thickeners, gels and sets quickly enough to avoid draining and sagging, while still allowing ample flow time for controlled application periods. We recommend this hardener when "overnight" sandibility is more important than continuous laminating and open time (as provided by MAS Slow Hardener) MAS Medium will also provide a beautifully smooth void free finish, with great resistance to milking out during application and fogging in critical clear coating applications. MAS Medium's cure speed may be adjusted by the addition of MAS Fast or MAS Slow hardeners. The 2:1 mix ratio of resin : hardener should be maintained, regardless of hardener blend.

STORAGE LIFE: A minimum of 12 months in a sealed container at ambient temperatures.

Color (Gardener) 3
Viscosity @77° F, cp 200 unmixed, 410 mixed
Specific Gravity @77° F 0.0998
Flash Point (closed cup) °F 234
Mix Ratio: 2:1 Resin to Hardener
Mixed Viscosity (2072/718) @77° F 400-500 cps
Gel Time, mins (150g mix@77° F) 23
Thin Film Set Time, hrs @77° F 4
Thin Film Set Time, hrs@41° F 22
Peak Exotherm, °F (100mg mix @77° F) 250
Peak Exotherm Time, mins. 29
Cure Time 2-7 Days

Mas Medium Hardener, 27.5 Gallons

Best Use A Polyamine Blend Intended for Moderate Reactivity
Capacity 27.5 Gallons
Cure Time 4 Hours Working
Type Two-Part Epoxy Resin Hardener